Investigation of a cycloaliphatic epoxy resin system considering Al ₂O₃ and TiO₂ nanofillers

authored by

Mohammad Mahdi Saei Shirazi, H. Borsi, Ernst Gockenbach

Abstract

Inorganic nanofillers combined with organic polymers have been used for several years in order to enhance the electrical and dielectric properties of insulation materials. The advantages of using nanofillers can be explained by very large interface area of them in comparison with microfillers. To evaluate the influence of Al₂O₃and also γ-TiO ₂nanofillers separately on a cycloaliphatic epoxy resin system as an outdoor insulation system, specific DC volume resistivity, loss factor and permittivity were investigated. In this regard, several specimens with 2 mm thickness were produced containing 0%, 1%, 3%, 5% and 7% per weight under especial condition to have the most possible homogeneous distribution of nanofillers. Then the behavior of the mentioned parameters was investigated from 23°C up to 170°C at different frequencies. According to the results, DC volume resistivity of the specimens with Al₂O₃ shows higher resistance between 80°C and 140°C than the specimens without nanofiller. Adding TiO₂ does not cause considerable changes in volume resistivity. Loss factor has no significant change up to glass transition temperature (Tg), but it reduces at the temperatures above Tg, when Al ₂O₃ or TiO₂ was added. Relative permittivity of the specimens containing Al₂O₃ and TiO₂ were increased up to 110 °C. After this temperature, relative permittivity of all nanocomposites decreases in comparison to 0 wt. %.

Organisation(s)

High Voltage Engineering and Asset Management Section (Schering Institute)

Type

Conference contribution

Pages

186-189

No. of pages

4

Publication date

2012

Publication status

Published

Peer reviewed

Yes

ASJC Scopus subject areas

Electrical and Electronic Engineering

Electronic version(s)

https://doi.org/10.1109/ICHVE.2012.6357072 (Access: Unknown)